High Speed PLA
SUNLU High Speed PLA is optimized for high-speed printing, offering excellent flowability and dimensional stability, suitable for rapid prototyping and batch production.
Diameter：
Weight：
SUNLU High Speed PLA
Supports printing speeds up to 600 mm/s
Supports printing speeds up to 600 mm/s, greatly improving efficiency
This material supports printing speeds of up to 600mm/s, significantly enhancing printing efficiency and effectively reducing model formation time. Whether for rapid prototyping or batch production, it easily handles the task, greatly improving overall work efficiency.
Neat filament winding, reducing tangling and clogging risk
Using a precision winding process, the filament is tightly and orderly coiled, effectively reducing tangling, knotting, and clogging risks. This ensures a smooth and stable printing process, reducing the likelihood of printing failures.
1.75 ± 0.02 mm diameter tolerance, high printer compatibility
The filament diameter is strictly controlled within the range of 1.75±0.02mm, ensuring consistent and stable extrusion. This improves print accuracy and surface quality, while also offering better compatibility with various printers.
Compatible with 99% of FDM printers on the market
Compatible with 99% of FDM 3D printers on the market, this material offers strong compatibility, requiring no complex adjustments for easy use. It meets the printing needs of different users and devices.
Parameter Information
| Mechanical Properties | Physical Properties | Print Settings | |||
|---|---|---|---|---|---|
| Tensile Strength（MPa） | 39±5 | Density（g/cm³） | 1.28 | Nozzle Temperature & Print Speed | 210-230℃ / ≤250mm/s |
| Flexural Strength（MPa） | 70±5 | Melt Flow Index（g/10 min） | 7±2.5 | Bed Temperature | 50-60℃ |
| Notched Izod Impact Strength（kJ/m²） | 4.5±2 | Shrinkage（%） | 0.1-0.3 | Retraction Distance | 0.8-1.2mm |
| Elongation at Break（%） | 12±4 | Heat Deflection Temperature（℃） | 57±4 | Retraction Speed | 30-40mm/s |
| Shore Hardness（HA/HD） | 81.4 | Vicat Softening Temperature（℃） | 54 | ||